商品用途：主要用于空调机、主装式空调机组、冰箱、冰柜、太阳能、热水器、壁挂炉等
商品特点：该产品具有内外表面高清洁、超光亮、组织均匀致密、尺寸精度高、换热效率高、易焊接、耐腐蚀、使用成型性好等优点
执行标准：GB/T17791
下表列出外径、壁厚等参数
|
规格 |
状态 |
平均外径(mm) |
平均壁厚(mm) |
最大运行压力(Mpa) |
爆破压力(Mpa) |
|
φ6.35*0.8 |
M |
6.35 |
0.77 |
13.43 |
61.77 |
|
φ6*0.5 |
M |
6 |
0.48 |
8.55 |
39.32 |
|
φ6*0.6 |
M |
6 |
0.58 |
10.48 |
48.19 |
|
φ6*0.55 |
M |
6 |
0.53 |
9.51 |
43.72 |
|
φ6.35*0.6 |
M |
6.35 |
0.58 |
9.85 |
45.33 |
|
φ6*0.4 |
M |
6 |
0.39 |
6.86 |
31.54 |
|
φ6*0.45 |
M |
6 |
0.43 |
7.6 |
34.97 |
|
φ6.35*0.65 |
M |
6.35 |
0.63 |
10.78 |
49.57 |
|
φ6*0.65 |
M |
6 |
0.63 |
11.46 |
52.73 |
|
φ6.35*0.7 |
M |
6.35 |
0.68 |
11.71 |
53.88 |
|
φ6*0.8 |
M |
6 |
0.77 |
14.3 |
65.79 |
|
φ6*1 |
M |
6 |
0.97 |
18.57 |
85.41 |
|
φ7.5*0.4 |
M |
7.5 |
0.39 |
5.43 |
24.96 |
|
φ7.94*0.65 |
M |
7.94 |
0.63 |
8.47 |
38.97 |
|
φ8*0.6 |
M |
8 |
0.58 |
7.7 |
35.4 |
|
φ8*1.0 |
M |
8 |
0.97 |
13.43 |
61.77 |
|
φ8*0.65 |
M |
8 |
0.63 |
8.4 |
38.66 |
|
φ9.52*0.6 |
M |
9.52 |
0.58 |
6.4 |
29.46 |
|
φ9.52*0.8 |
M |
9.52 |
0.77 |
8.65 |
39.78 |
|
φ9.52*0.5 |
M |
9.52 |
0.48 |
5.25 |
24.17 |
|
φ9.52*0.45 |
M |
9.52 |
0.44 |
4.8 |
22.08 |
|
φ9.52*0.5 |
M |
9.52 |
0.49 |
5.37 |
24.69 |
|
φ9.52*0.35 |
M |
9.52 |
0.34 |
3.68 |
16.9 |
|
φ9.52*0.65 |
M |
9.52 |
0.63 |
6.99 |
32.14 |
|
φ10*1 |
M |
10 |
0.97 |
10.52 |
48.37 |
参数说明：
1.表中各个规格的最大运行压力根据理论公式计算得出，部分规格做过验证试验，但由于铜管本身存在尺寸差异以及细微
缺陷，因此上表压力数值仅供参考，新机型或新运行环境设计仍需实际验证作为依据
2.铜管经过弯制、扩口、胀管、攻丝等操作后机械性能和局部尺寸会发生变化，实际应用中需要考虑在内
连铸连轧：
连铸工艺----采用等压铸造与电磁改性新技术，稳定铸造液面，消除铸坯裂纹，细化铸坯晶粒，提高产品性能
轧管工艺----采用新辊型、新型芯棒头和轧辊连接新结构技术，通过提高轧制温度，使轧管晶粒更均匀，减少
轧辊窜动，从而进一步提高了轧管同心度
拉伸工艺----采用三联拉与防共振盘拉组合拉伸新技术，减轻管间擦伤，减弱管外表面纵向缺陷，减小壁厚偏
差，显著提高了铜管尺寸精度和同心度
涡流探伤：
利用电磁感应原理，检测导电构件表面和近表面缺陷的一种探伤方法。通过涡流探伤的铜管，在有缺陷和隐
患的地方喷涂上40公分左右长度的黑墨，在安装使用一定将其喷墨部分去掉从而保证使用质量
清洗脱油：使铜管内壁达到R410A冷煤的使用条件
0